cr12mov gun si mo de deng wen cui huo
Author(s): 
Pages: 51-52
Year: Issue:  6
Journal: Heat Treatment of Metals

Keyword:  等温淬火分级淬火滚丝模使用寿命模具热处理下贝氏体显微裂纹残余奥氏体硬度值断裂韧性;
Abstract: <正> 我厂521-612分电器螺塞的螺纹加工是在228-33滚丝机上进行的。长期以来,由于模具崩刃严重,使用寿命不高。我们根据钢的组织对断裂韧性的影响,联系到模具脆性断裂的宏观特征与针状马氏体的显微裂纹之间的关系,认为崩刃是由于显微裂纹扩展所造成的,因而选定硬度较高、韧性和塑性较好、没有显微裂纹的下贝氏体组织结构,以期达到提高使用寿命的目的。另外,模具要求 HRC54-56,按一般分级淬火要能准确控制比较困难,加之高温回火造成模具表面腐蚀,这些都试图通过等温淬火加以解决。