yi xi zhuang zhi xi shi zheng qi fa sheng qi fu shi yuan yin fen xi
Author(s): 
Pages: 23-25
Year: Issue:  1
Journal: Qilu Petrochemical Technology

Keyword:  设计能力蒸汽发生器乙烯装置工艺水腐蚀原因分析内漏解决办法稀释蒸汽运行比较;
Abstract: <正> 齐鲁乙烯装置投产4年多以来,装置运行比较平稳,但一直未能达到设计能力。影响装置达标的因素很多,单就裂解单元稀释蒸汽发生器(EA—123)而言,就多次发生腐蚀内漏。这也是制约乙烯装置投料量的一个重要因素。为此,对EA—123产生腐蚀的原因进行了探讨,并试图找出根本性的解决办法。一、EA—123的运行情况 EA—123A、B、C、D是利用油急冷塔(DA—101)塔釜来的急冷油与工艺水换热,并将工艺水汽化产生裂解用稀释蒸汽,其物